1.Key application areas
Rubber Industry:
Tyre vulcanisation:
Sulphur + accelerator (CBS 1.2phr + S₈ 2.5phr)
Crosslink density: 4×10-⁴ mol/cm³
30% reduction in dynamic heat generation
Sealing products:
Peroxide vulcanised EPDM (DCP 1.5%)
Compression permanent deformation <20% (150℃×70h)
Plastic modification:
Cross-linked polyethylene (XLPE):
Silane grafting method (VTMS 2% + catalyst)
Temperature resistance grade from 70°C → 90°C
Breakdown strength >30kV/mm
Polypropylene foaming:
Radiation crosslinking (electron beam 50kGy)
Bubble density＞10⁶ cells/cm³
Biomaterials:
Hydrogel:
Photoinitiated crosslinking (Irgacure 2959 0.1%)
Dissolution rate >500 per cent
Cytocompatibility >95%
Medical catheters:
Peroxide cross-linked silicone rubber
Tear strength >30kN/m
2 Typical problem solutions
Uneven crosslinking:
Cause: Poor dispersion or temperature gradient
Countermeasure:
Use twin-screw extruder (shear rate > 500s-¹)
Temperature rise in stages (e.g. 120°C → 160°C step vulcanisation)
Side reaction control:
Peroxide system pre-crosslinking:
Addition of TAIC (Triallyl Isocyanurate) 1 per cent.
Coking time extended to >10min (160°C)
Insufficient cross-linking:
Silane cross-linked polyethylene:
Increase hydrolysis temperature to 90°C
Add dibutyltin dilaurate (0.1%)
Kontaktieren Sie uns jetzt!
Wenn Sie einen Preis benötigen, tragen Sie bitte Ihre Kontaktdaten in das unten stehende Formular ein. Wir werden uns in der Regel innerhalb von 24 Stunden mit Ihnen in Verbindung setzen. Sie können mir auch mailen info@changhongchemical.com während der Geschäftszeiten ( 8:30 bis 18:00 Uhr UTC+8 Mo.~Sa. ) oder nutzen Sie den Live-Chat auf der Website, um eine schnelle Antwort zu erhalten.
Related product references: For formulation review or sourcing comparison, see CHLUMIAO HO-17/17EH.